Daye Uhpc Material Construction Material Macro Fiber

• Customization: Available
• Application: Construction, Alternative Concrete Panel Structure
• Function: Strengthen
• Model NO.: PP50, PP15, PP19
• Product Name: Macro Synthetic Fiber
• Skill: Advanced Technology Abroad
• Appearance: White, or Black, Embossed
• Moisture Content: ≤0%
• Acid&Alkali Resistance: Excellent
• Melt Flow: 3.5
• Density: 0.91g/cm3
• Melt Point: 170ºC
• Fibre Dimension: L: 65mm
• Modulus: >10 Gmpa
• Minimum Tensile Strength: >650 MPa
• Production Time: 15-20 Days
• Application Scenarios: Industrial Architecture
• Design Style: Contemporary
• Material: Polypropylene Fiber
• Certification: CE, ISO
• After-sales Service: Online Technical Support
• Warranty: 1 Year
• Type: Macro Synthetic Fibre
• Transport Package: Paper Bag Pallet Container
• Specification: 0.8-12mm, 40 30 50mm
• Trademark: DAYE
• Origin: Jiangxi Ganzhou
• HS Code: 7326201000
• Production Capacity: 10000 Tons/Year

Product Description

Macro Synthetic Fibre
Description
    The fibres are Made of Polypropylene.
Features

• Provides good impact,fatigue,shrinkage control and ductility in all grade concretes.
• Cost saving,Is easier to use,to disperse and safe to handle.
• Can be used in highly corrosive circumstance.
• The surface has been embossed,which greatly improves the cohesive force between fibres and concrete,and also boosts shrinkage resistance and crack resistance.
• The toughness of macro synthetic fibre is less stronger than steel fibre.But test has shown slabs on grade and pre-cast concrete predominately require a dosage rate of between 25kg-40kg of steel fibres per cubic meter, in comparison,using between 3kg-10kg of macro synthetic fibre per cubic meter of concrete. Synthetic fibres achieve greater strength and ductility in the matrix.

Technical Information

Minimum Tensile Strength	>650 MPa
Modulus	>10 GMPa
Fibre dimension	L: 65mm;
Melt Point	170ºC
Density	0.91g/cm^3
Melt flow	3.5

Acrylic fibre
Description:
Polyacrylonitrile fiber is a new type of concrete fiber produced by American advanced technology.In the engineering field has the third generation of concrete special fiber reputation.The fiber is using a special plant in the high and cold area as raw material, refined by special chemical and physical process, and has the characteristics of natural affinity and high strength and high mold, which can effectively improve the mechanical properties of concrete, freezing and thawing resistance and seepage resistance.

Technical Information:

fibre material	100% polypropylene	density	1.18g / cubic cm
Fiber type	monofilament	initial modulus	Greater than et al 1.18 than 10.0Gpa
tensile strength	Greater than 910Mpa	equivalent diameter	13+-1um
elongation at break	20+-5%	fibre number	1.90+-0.2dtex
fibre length	6,10,12,15	temperature tolerance	good
pigment	yellowish	light permanency	good

Polypropylene mesh fibers
Description:
Polypropylene mesh fiber, also known as polypropylene fiber mesh, is made of polypropylene as the raw material, through a special production process.Its appearance is mostly a network structure made of multiple fiber single filaments cross-linking. After the addition of functional maternal modification and special surface treatment technology, it has excellent dispersion and good hydrophilic properties in concrete.When polypropylene mesh fiber into the concrete, in the process of concrete mixing, the lateral connection between the fiber single filament by the concrete rubbing and friction and tear, forming fiber single filament or mesh structure fully open, can have more than 7 million fibers per cubic meter of concrete, its rough tear edge between the fiber and concrete has excellent grip, thus improve the performance of the concrete.
Technical Information:

density	0.91+-0.01	modulus of elasticity	More than 3500
length	12,15,19,38	equivalent diameter	100+-50
Fiber shape	reticulation	Crack elongation rate	5-10
Acid and alkali resistance	mightiness	hydrophilism	NO
tensile strength	450Mpa	fusing point	The 160-170 Degrees