Plastic Concrete Polyvinyl Alcohol PVA Fiber Replacement Synthetic Fibre

• Customization: Available
• Application: Concrete Reinforcement
• Color: White
• Model NO.: DY282- POM Fiber 12MM
• Length: 12mm
• Material: Polyoxymethylene
• Tenacity: 967-1175 MPa
• Type: POM Fiber
• Product Name: POM Polyformaldehyde Monofilament Synthetic Fiber
• Density: 1.41g/cm3
• Melting Point: 165 Celsius
• Glass Transition Temperature: -30 Celsius
• Working Temperature: -45~95 Celsius
• Linear Density (Dtex): 450±90
• Young′s Modulus: 8.8 Gpa
• Elongation at Breakage: 18 %
• Dosage by Volume: 1-3 %
• Dosage: 14.2-42.6kg/M3
• Alkali Resistance: 99 %
• Production Time: 15-20 Days
• Payment: 30% T/T Prepaid, 70% Against Copy of B/L
• Function: Strengthen, Anti-Knock
• After-Sales Service: Online Technical Support
• Transport Package: Damp-Proof Poly Bag
• Specification: 0.2 x 12 MM
• Trademark: DAYE
• Origin: China Ganzhou
• HS Code: 5503900000
• Production Capacity: 10000 Tons/Year
• Package Size: 38.00cm * 38.00cm * 36.00cm
• Package Gross Weight: 6.000kg
• Lead Time: 3 days (1 - 1000 Kilogram/Kilograms) ; 7 days (1001 - 3500 Kilogram/Kilograms) ; To be negotiated ( > 3500 Kilogram/Kilograms)

Product Description

Product Name	UHPC Special Synthetic Fiber
Diameter (mm)	0.2±0.02
Linear density (dtex)	450±90
Breaking tenacity (MPa)	≥ 967
Elongation at break (%)	≤ 18
Elastic modulus (MPa)	≥ 8800
Length (mm)	4 ,6 ,8 ,12 ,16 ,24 ,30±1

1. High tensile strength and modulus: Tensile strength can be 1100 Mpa and modulus is 10 GPa.

2. Pretty good high temperature anti-knock performance: Friction and wear Resistant.

3. Excellent chemical resistance: Tensile strength can still keep 99 per cent of itself when it is in 10 per cent sodium hydroxide alkaline environment.

4. Extremely wide using temperatures: It can stand temperatures from -45 to 95 Celsius.

 

After adding POM(Polyformaldehyde/Polyoxymethylene) fiber, UHPC(Ultra High Performance Concrete) parts can achieve the following features:

1. Lightweight: The density of POM fiber is 1.41 g/cm³, while that of steel fiber is 7.8 g/cm³.

2. Toughened: The damage of matrix brittle without warning will be decreased.

3. Durable and rust free: Alkali resistant since POM fibers are mixed in UHPC.

4. Easy to shape: When UHPC parts are shaping, they can maintain high liquidity due to good interface affinity.

5. Filled evenly and densely: Dispersion of POM fiber is very good. It has higher stiffness and dispersibility, and lower air entrainment than other types of fibers.

6. Safe to use: As there is no risk of exposed fibers in finished products, they can be touched directly.